Quote:
Originally Posted by Butterman
I know it's been a while and I'm not sure if someone's told you since but rods snapping under deccel at high rpm is very common for a couple reasons. So by looking at your rod it's clear that it failed under tension, because it's torn in half and not bent, which indicates that it failed during deccel.
|
How would one go about preventing this from happening? Avoid lifting at high rpm?