Quote:
Originally Posted by smudge
We're not seeing any signs of oil starvation for any of the components. The oil report from Millers shows that the oil performance was satisfactory
The small end looks to have let go and then caused the rod to windmill around and smash into pieces when hitting the block
All parts are being sent off to Japan to be investigated
|
understood
I know you're committed to the HKS parts but I would highly recommend sourcing a rod with a copper beryliium bush on the little end if you can
unless the HKS part does actually have this?