Originally Posted by Tcoat
How badly has it hit? Are there marks underneath? I ask because as much as it would certainly appear to be a bad weld it could also have been broke off by repeated hits.
|
I don't know about the hitting or melting, but that is most definitely a bad weld. Look at the last pic he posted of the hanger. The weld is undercut. It would most likely be undercut on the pipe also, which would make the metal thin and weak right there. It's no wonder it cut loose.
Banging it on the ground didn't help, but a proper weld should have held anyway.