Too many edits. Okay so the area that the wrist pin spreads the forces is much greater, that makes sense. Thanks. I see why it makes sense to use it in frequently rebuilt engines, you can cut down the mass significantly, and the aluminum rod will still survive a respectable amount of time, but if you want to increase the service life the aluminum rod needs significant strengthening which would not be worthwhile.
|